Swash plate and production method of the same

ABSTRACT

A swash plate  3  includes a substrate  11  made of an iron-based material, a hard first resin layer  12  provided to coat an end surface of the substrate  11 , and a soft second resin layer  13  provided to coat the first resin layer  12 . A spiral annular groove  12 A is formed in a surface of the first resin layer  12 , and the second resin layer  13  is provided to match the sectional shape of the first resin layer  12 . With the soft second resin layer  13  on a sliding surface  3 A of the swash plate  3 , a swash plate  3  having a good fit in an initial stage of sliding can be provided. When the second resin layer  13  partially wears, a protrusion  12  of the first resin layer  12  of the hard resin is exposed to provide good wear resistance and good sliding properties.

TECHNICAL FIELD

The present invention relates to a swash plate and a production methodthereof, and more particularly to a swash plate for a swash plate typecompressor mounted in an automobile and a production method thereof.

BACKGROUND ART

A conventionally known swash plate type compressor includes a swashplate rotated by a rotating shaft, a plurality of shoes that slide withrespect to the swash plate, and a plurality of pistons that slide withrespect to the plurality of shoes and reciprocate (for example, Patentdocument 1).

For such a conventional swash plate type compressor, to improve thesliding properties between the shoe and the swash plate, it has beenproposed that, for example, an end of the shoe is formed to have aconvex shape with a high middle side or a sliding surface of the swashplate is improved (Patent documents 2 and 3). Also, to improve thesliding properties, proposals have been made on an improvement in asliding surface of a bearing as a sliding member or in a material (forexample, Patent documents 4 to 6).

PRIOR ART DOCUMENTS

Patent document 1: Japanese Patent Laid-Open No. 2008-185124

Patent document 2: National Re-publication of International PatentApplication No. WO2002-075172

Patent document 3: Japanese Patent Laid-Open No. 9-71899

Patent document 4: Japanese Patent Laid-Open No. 7-259863

Patent document 5: Japanese Patent Laid-Open No. 2002-39186

Patent document 6: Japanese Patent Laid-Open No. 2007-204602

SUMMARY OF THE INVENTION Technical Problem

Clutchless swash plate type compressors have been recently widely used.In such a clutchless swash plate type compressor, a swash plate isalways rotated in an operation state of an engine of an automobile. Inthis case, a variable capacity swash plate type compressor is aprecondition, and when a car air conditioner is not used, the swashplate is maintained perpendicularly to a rotating shaft. In this state,a piston of the swash plate type compressor does not reciprocate, andthus a coolant and mist-like lubricating oil are not circulated in acylinder of the swash plate compressor. Specifically, since the coolantand the mist-like lubricating oil are not circulated in the swash platetype compressor, an insufficient amount of lubricating oil is suppliedto a sliding portion between the swash plate and the shoe to cause poorlubrication. Further, the coolant itself washes the lubricating oil, andthe sliding portion between the swash plate and the shoe easily fallsunder a boundary lubrication condition due to a dry sliding condition.Thus, the clutchless swash plate type compressor has disadvantages inthat the frictional heat in sliding between the shoe and the swash plateincreases the wear of a resin layer that forms a sliding surface of theswash plate, or seizure of the resin layer of the swash plate occurs.

Also, for a swash plate with a sliding surface coated with a resinlayer, wear of the resin layer causes a plated layer or a metal layer asan intermediate layer to be exposed and easily causes seizure.

It may be conceivable to use, as a swash plate, a sliding memberdisclosed in Patent Literature 4, that is, a sliding member including ametal material placed on a surface of a substrate and having an annulargroove in a surface. However, the sliding member in Patent document 4 isa plain bearing of a crankshaft, and for the plain bearing, sufficientlubricating oil is forcedly supplied to a sliding surface. Thus, thesliding member in Patent Literature 4 can obtain sufficient slidingproperties as the plain bearing. However, if the sliding member inPatent Literature 4 is used as a swash plate in the poor lubricationstate as described above, the metal swash plate comes into contact withthe metal shoe to easily cause seizure on the sliding surface.

Solution to Problem

In view of the above-described circumstances, the present inventionprovides a swash plate having a sliding surface that slides with respectto a shoe, including: a substrate made of any of iron-, aluminum-, orcopper-based materials; a hard first resin layer provided to coat asurface of the substrate and having an annular groove formed in an outerside surface; and a soft second resin layer provided to coat the surfaceof the first resin layer and formed to match a sectional shape of theannular groove in the first resin layer, wherein in an initial stage ofsliding with respect to the shoe, the second resin layer is the slidingsurface, and when the second resin layer partially wears and aprotrusion of the annular groove in the first resin layer is exposed,the protrusion and the second resin layer adjacent to the protrusion arethe sliding surface.

The present invention provides a production method of a swash plate,including the steps of: applying a resin paint for a first resin layercomposed of a hard resin to an end surface of a substrate to provide thefirst resin layer; drying and/or baking the first resin layer and thenforming a minute annular groove in a surface of the first resin layer;applying a resin paint for a second resin layer composed of a soft resinto the first resin layer provided with the annular groove; then rotatingthe substrate at high speeds to remove unnecessary parts of the resinpaint for the second resin layer; and forming the second resin layer tomatch the sectional shape of the surface of the first resin layer.

Effects of Invention

According to the above-described configuration, the soft second resinlayer is the sliding surface in the initial stage of sliding, therebyproviding a swash plate having a good fit to the shoe. After slidingwith respect to the shoe, the hard first resin layer is exposed as thesliding surface and slides with respect to the shoe, thereby providing aswash plate having a good wear resistance.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a sectional view of the essential portions of an embodiment ofthe present invention.

FIG. 2 is an enlarged sectional view of the essential portions of aswash plate 3 shown in FIG. 1.

FIG. 3 is a sectional view of the portion shown in FIG. 2 partially wornand a perspective view of a surface shown together.

FIG. 4 shows a difference in sliding properties between the embodimentof the present invention and comparative members.

DESCRIPTION OF THE EMBODIMENTS

Now, the present invention will be described based on a shownembodiment. In FIG. 1, reference numeral 1 denotes a sliding deviceprovided in a housing of a variable capacity swash plate typecompressor. The sliding device 1 includes a swash plate 3 mounted to arotating shaft 2 journaled in the housing, and a plurality of shoes 4that slide with respect to the swash plate 3.

The swash plate 3 is formed into a disk shape, and opposite end surfacesof the swash plate 3 are sliding surfaces 3A and 3B that slide withrespect to the shoes 4. The swash plate 3 is adjusted in inclinationangle with respect to the rotating shaft 2 by an unshown inclinationangle adjustment means. Meanwhile, the shoe 4 is generally made of asemi-spherical metal and has a flat sliding surface 4A that slides withrespect to the sliding surface 3A or 3B of the swash plate 3 and asemi-spherical surface 4B.

In the housing of the swash plate type compressor, a plurality ofpistons 5 are provided in parallel with and surround the rotating shaft2. A pair of shoes 4 are slidably held in a notch 5A formed in one endof each piston 5, the notch 5A in that state is placed to cover an outerperipheral portion of the swash plate 3 and sliding surfaces 4A of eachpair of shoes 4 are abutted against the sliding surfaces 3A and 3B ofthe swash plate 3. The other end of each piston 5 is slidably fitted inan unshown cylinder provided in the housing.

When the rotating shaft 2 is rotated, the swash plate 3 is rotated, andthe sliding surfaces 3A and 3B that are opposite end surfaces of theswash plate 3 slide with respect to the sliding surfaces 4A of each pairof shoes 4, which moves each piston 5 forward and backward in thecylinder via each pair of shoes 4. The above-described configuration isthe same as that of a conventionally known sliding device.

Thus, in this embodiment, the sliding surfaces 3A and 38 that areopposite end surfaces of the swash plate 3 are improved as describedbelow to improve the sliding properties of the swash plate 3.

Specifically, as shown in a sectional view of the essential portions inFIG. 2, the swash plate 3 of this embodiment has a disk-shapediron-based substrate 11 with a flat surface, and a first resin layer 12of a hard resin is provided to coat the entire surface of one endsurface 11A of the substrate 11.

In this embodiment, as a material for the first resin layer 12, amaterial is used composed of a thermosetting resin binder to which atleast one of graphite, carbon, MoS2 and PTFE is added. Adding a hardmaterial such as alumina besides any of the above-described additivescan further increase the strength of the first resin layer 12.

The thermosetting resin binder can include, for example, a polyimideresin (PI), a polyamide-imide resin (PAI), an epoxy resin, a phenolresin, a polyamide (nylon), and an elastomer. Specifically, athermosetting resin binder such as a varnish of an aromatic polyimide,polyether imide, polyester imide or aromatic polyamide-imide, ordiisocyanate-, BPDA-, sulfone-modified resin thereof are preferablyused.

The graphite and carbon preferably have a high crystallinity.Particularly, a preferable spacing is 3.5 angstroms or less, whichreduces the variations in friction coefficient in sliding. The graphiteand carbon may be natural or artificial ones, but the artificialgraphite and carbon are preferable in terms of wear resistance, and thenatural graphite and carbon are preferable in terms of seizureresistance and low friction. An average particle diameter of thegraphite and carbon is not particularly limited, but graphite and carbonhaving an average particle diameter of 10 μm or more are used to furtherimprove the wear resistance when a load is applied. Meanwhile, graphiteand carbon having an average particle diameter of less than 10 μm arepreferably used to finely disperse the graphite and carbon in thethermosetting resin binder to provide good wear properties to the binderand further reduce variations in the friction coefficient. Thus,graphite and carbon having the average particle diameter of 10 μm ormore and graphite and carbon having the average particle diameter ofless than 10 μm are preferably used at an appropriate ratio incombination.

Particularly preferable, the PTFE is a granular baked PTFE. The bakedPTFE is prepared by heating (baking) PTFE powder obtained by suspensionpolymerization or emulsion polymerization to a melting temperature andthen grinding the powder, or prepared by compressing and shaping thepowder before baking and grinding the powder after the baking. Aparticularly preferable PTFE is obtained by once shaping powder obtainedby suspension polymerization and then baking and grinding the powder.Such baked powder can be used to obtain a relatively hard PTFE, good lowfriction properties, and also good wear resistance.

The baked PTFE is granular and an average particle diameter thereof isnot particularly limited, but PTFE having an average particle diameterof 7 μm or more is used to achieve better low friction properties andalso better wear resistance. Meanwhile, PTFE having an average particlediameter of less than 7 μm is preferably used to finely disperse thePTFE in the thermosetting resin binder to provide good frictionproperties to the thermosetting resin binder. Thus, the PTFE having theaverage particle diameter of 7 μm or more and the PTFE having theaverage particle diameter of less than 7 μm are preferably used at anappropriate ratio in combination.

The first resin layer 12 preferably has a component composition of 10%to 50% by mass of graphite, the balance being the thermosetting resinbinder, and MoS₂ or PTFE may be added as required within a range of 1%to 30% by mass. The amount of PTFE is smaller than that of MoS₂ and thetotal amount of PTFE and MoS₂ is smaller than that of graphite.

A spiral annular groove 12A is formed across the entire surface of thefirst resin layer 12 in a circumferential direction at radially regularpitches. The height of a protrusion 12B of the annular groove 12A, thatis, the depth of a recess 12C of the annular groove 12A, is the sameacross the entire surface of the first resin layer 12.

Further, a second resin layer 13 is provided to coat the entire surfaceof the first resin layer 12 formed with the annular groove 12A. As amaterial for the second resin layer 13 of a soft resin, a thermosettingresin binder is used to which at least one of low friction materialssuch as MoS₂ or PTFE is added.

The second resin layer 13 has a component composition of 30% to 80% bymass of MoS₂, the balance being the thermosetting resin binder, and PTFEmay be added as required within a range of 1% to 30% by mass. The amountof PTFE added is smaller than that of MoS₂.

Since the second resin layer 13 is provided to match the sectional shapeof the surface of the first resin layer 12, a spiral annular groove 14matching the surface shape of the first resin layer 12 is maintained ina surface that forms the sliding surface 3A. The swash plate 3 isproduced via a production process described later and, thus, extremelyminute countless irregularities are formed in the entire surface of thesecond resin layer 13. This can improve the holding properties oflubricating oil in the surface of the second resin layer 13, that is,the sliding surface 3A.

The thickness t1 of the first resin layer 12 is about several to 30times larger than the thickness t2 of the second resin layer. Thethicknesses t1 and t2 herein refer to thicknesses at a position of a topof the protrusion 12B.

The thickness A of a portion of the second resin layer 13 at the recess12C is slightly larger than the thickness B of a portion of the secondresin layer 13 at the top of the protrusion 12B. More specifically, thesize relationship thereof is 3/2A≧B.

Based on the thickness relationship of the resin layers 12 and 13described above, in this embodiment, the thickness of the first resinlayer 12 is set to 3 to 70 μm, while the thickness of the second resinlayer 13 is set to 1 to 40 μm. More preferably, the thickness of thefirst resin layer 12 is 5 to 50 μm and the thickness of the second resinlayer 13 is 3 to 10 μm.

In this embodiment, one sliding surface 3A of the swash plate 3 isformed as described above, and the other sliding surface 3B not shown inFIG. 2 is also formed in the same manner as the sliding surface 3A.

As described above, in the swash plate 3 of this embodiment, the surfaceof the substrate 11 is coated with the first resin layer 12, the annulargroove 12A is formed across the entire surface of the first resin layer12, and the surface of the first resin layer 12 is further coated withthe second resin layer 13. Specifically, an intermediate layerconventionally provided between the substrate 11 and the resin layer isomitted in this embodiment.

Next, a production process of the swash plate 3 of this embodiment willbe described. Specifically, in this embodiment, the disk-shapedsubstrate 11 made of an iron-based material is first prepared. Then, athermosetting resin binder and at least one of graphite, carbon, MoS₂and PTFE are mixed with a proper amount of organic solvent to prepare aresin paint for the first resin layer 12. The organic solvent adjuststhe viscosity and facilitates mixing and any organic solvent may be usedwithout limitation as long as it can dissolve a thermosetting resinbinder. For example, when the thermosetting resin binder ispolyamide-imide, xylene, N-methyl-2-pyrolidone, toluene, or the like maybe used.

Then, the resin paint for the first resin layer is applied to flatopposite end surfaces of the substrate 11, and dried or/baked. As apainting method, for example, spray painting, roll painting,electrostatic painting or stamping painting may be used. Thus, the firstresin layer 12 is formed to coat the opposite end surfaces of thesubstrate 11. Adding a hard material such as alumina besides theabove-described additives can further increase the strength of the firstresin layer 12.

Next, after the resin layer 12 on the opposite end surfaces is driedand/or baked, the annular groove 12A is formed across the enter surfaceof the first resin layer 12 in a circumferential direction at radiallyregular pitches. The annular groove 12A may be formed by cutting with alathe or transferring a groove shape with a press or a roller.

Further, a resin paint for the second resin layer 13 separately preparedis applied to coat the entire surface of the first resin layer 12 formedwith the annular groove 12A. The resin painting for the second resinlayer 13 is a mixture of a thermosetting resin binder and at least oneof low friction materials such as MoS₂ or PTFE with a proper amount ofan organic solvent, and is applied to the entire surface of the firstresin layer 12 formed with the annular groove 12A. Then, a through holeat the center of the substrate 11 is fitted on a drive shaft to rotatethe substrate 11 at high speeds for a desired time. Thus, an excess ofthe resin paint for the second resin layer applied to the surface of thefirst resin layer 12 is thrown off by a centrifugal force and removed.

Then, the resin paint is again dried and/or baked. Thus, the secondresin layer 13 in this embodiment is provided to have theabove-described thickness so as to match the sectional shape of thesurface of the first resin layer 12, and the above-described minutecountless irregularities are formed in the entire surface of the secondresin layer 13. As such, the swash plate 3 of this embodiment isproduced.

The minute countless irregularities may be formed in the entire surfaceof the second resin layer 13 of the swash plate 3 of this embodiment forthe following reasons. Specifically, in this embodiment, the mixture ofthe thermosetting resin binder to which MoS₂ or the like is added withthe organic solvent is used as the resin paint for the second resinlayer 13. Specifically, the resin paint for the second resin layer 13 inwhich countless particles of MoS₂ are evenly mixed in the liquidthermosetting resin binder is applied to the surface of the first resinlayer 12. Then, when the substrate 11 is rotated, from the resin paintfor the second resin layer 13, the thermosetting resin binder located onthe side closest to the surface is thrown off by the centrifugal force,and also the surface side of the thermosetting resin binder coating eachparticle of MoS₂ is thrown off. Thus, the countless particles of MoS₂mixed in the thermosetting resin binder are exposed on the surface, andthe thermosetting resin binder is dried and baked in that state. Thus,it is supposed that countless particles of MoS₂ are exposed on thesurface of the cured thermosetting resin binder and, thus, countlessminute irregularities are formed across the entire surface of the secondresin layer 13 in the embodiment.

The second resin layer 13 may be formed by the following method.Specifically, with the substrate 11 being rotated, the resin paint forthe second resin layer is applied to the central side of the first resinlayer 12 on the substrate 11. In this case, the substrate 11 is beingrotated, and thus the paint applied to the central side of the oppositeend surfaces of the substrate 11 is moved radially outwardly by thecentrifugal force, and an unnecessary resin paint for the second resinlayer is thrown off and removed. Thus, as the above-describedembodiment, the second resin layer 13 can be formed to match thesectional shape of the surface of the first resin layer 12 across theentire surface.

Then, immediately after the finish of the production, as shown in FIG.2, the entire surface of the sliding surface 3A (3B) of the swash plate3 of this embodiment is coated with the second resin layer 13.Specifically, in the swash plate 3 of this embodiment, the resin layer12 is not exposed to the surfaces of the sliding surfaces 3A and 3B inthe state before sliding with respect to the shoes 4 (the state in FIG.2). Thus, in an initial stage of sliding with respect to the shoe 4, thesecond resin layer 13 is the sliding surface 3A (3B) that slides withrespect to the sliding surface 4A of the shoe 4.

On the other hand, when time passes after the swash plate 3 is mountedto the rotating shaft 2 and then the sliding surfaces 3A and 3B slidewith respect to the sliding surface 4A of the shoe 4, the second resinlayer 13 coating the protrusion 12A and the top of the protrusion 12Awear (see FIG. 3). In this state, the top of the protrusion 12A of thefirst resin layer 12 and the second resin layer 13 adjacent thereto formthe sliding surface 3A (3B) and slide with respect to the slidingsurface 4A of the shoe 4.

According to the swash plate 3 of this embodiment, in the initial stageof sliding in which the sliding surfaces 3A and 3B start sliding withrespect to the sliding surface 4A of the shoe 4, the second resin layer13 of soft resin coating the top of the protrusion 12B wears to providea good fit of the sliding surfaces 3A and 3B of the swash plate 3.

Then, as shown in FIG. 3, when the protrusion 12B of the first resinlayer 12 and the second resin layer 13 adjacent thereto in the swashplate 3 wear due to sliding with respect to the shoe 4 and theprotrusion 12B is exposed, the protrusion 12B and the remaining portionof the second resin layer 13 adjacent thereto as the sliding surfaces 3Aand 3B slide with respect to the sliding surface 4A of the shoe 4.

In this state, the protrusion 12B of the first resin layer 12 of hardresin supports the shoe 4 and, in this state, the second resin layer 13of the soft resin also slides with respect to the sliding surface 4A ofthe shoe 4. Then, in this state, the lubricating oil is held in thecountless minute irregularities in the surface of the second resin layer13. This can maintain good seizure resistance and wear resistance of thesliding surfaces 3A and 3B in this embodiment.

FIG. 4 compares sliding properties between the swash plate 3 of thisembodiment configured as described above and swash plates 3 ofcomparative members 1 to 4 with surfaces of substrates 11 being coatedwith different coating layers. More specifically, the sliding propertiesof wear resistance, seizure resistance, oil holding properties and lowfriction are compared between this embodiment and the comparativemembers 1 to 4 under the condition of very poor lubrication.

In FIG. 4, POOR refers to no effect, FAIR refers to poor effect, GOODrefers to good, VERY GOOD refers to very good. The test conditions wereas described below.

Testing machine: High pressure atmosphere testing machine

RPM: 9500 rpm

Load: 16 MPa maximum

Type of oil: Mixture of refrigerating machine oil and coolant

Lubrication: Lubricant spraying

Counterpart shaft: SUJ2

As shown in FIG. 4, it is apparent that the swash plate 3 of thisembodiment has good wear resistance, very good seizure resistance andoil holding properties, and low frictional resistance.

Unlike this embodiment, in the comparative member 1, the surface of thesubstrate 11 was coated with a flat metal coating (Cu alloy spray layer)with an even thickness. For the comparative member 1, there were pooroil-holding properties and no effect of other sliding properties.Particularly, evaluation of wear resistance was impossible due toseizure.

In the comparative member 2, the surface of the substrate 11 was coatedwith a PTFE resin with an even thickness and the same annular groove asin this embodiment is provided in the surface. For the comparativemember 2, the wear resistance was good but other sliding properties werepoor or not effective. In the comparative member 3, the surface of thesubstrate 11 was coated with MoS₂ resin with an even thickness. For thecomparative member 3, the sliding properties other than wear resistancewere good but the wear resistance was not effective.

In the comparative member 4, the surface of the substrate 11 is coveredwith a mixed resin of PTFE resin and MoS₂ resin with an even thickness.For the comparative member 4, the sliding properties were generallypoor.

As shown in FIG. 4, it is apparent that the swash plate 3 of thisembodiment is superior in all the sliding properties.

As described above, the swash plate 3 of this embodiment has superiorsliding properties for the following reasons. Specifically, in thesurfaces of the sliding surfaces 3A and 3B of the swash plate 3, theannular groove 14 is generally maintained to match the annular groove12A in the first resin layer 12 and minute countless irregularities areformed in the entire surface of the second resin layer 13. Thus, thelubricating oil can be easily held in the sliding surfaces 3A and 3B toform an oil film. Thus, the oil film can be easily formed on the slidingsurfaces 3A and 3B and it is supposed that the swash plate 3 of thisembodiment has good oil-holding properties.

Also, in the initial stage of sliding in which the sliding surfaces 3Aand 3B of the swash plate 3 start sliding with respect to the slidingsurfaces 4A and 4B of the shoe 4, the portion of the second resin layer13 of the soft resin at the protrusion 12B wears, and thus the swashplate 3 of this embodiment has a good fit to the sliding surface 4A ofthe shoe 4.

Further, as shown in FIG. 3, when the second resin layer 13 coating thetop of the protrusion 12B wears and the protrusion 12B of the firstresin layer 12 is exposed, the protrusion 12B of the hard resin slideswith respect to the sliding surface 4A of the shoe 4 to prevent wear ofthe second resin layer 13. Also, it is supposed that the wearing powderysecond resin layer 13 adheres to the exposed protrusion 12B to improvethe wear resistance of the swash plate 3.

Also in the state shown in FIG. 3, there is the second resin layer 13adjacent to the exposed protrusion 12B of the exposed first resin layer12 and thus the lubricating oil is held in the second resin layer 13.Thus, it is supposed that the swash plate 3 of this embodiment also hasa good seizure resistance.

As described above, according to the swash plate 3 and the productionmethod thereof of this embodiment, the swash plate 3 having a high wearresistance and seizure resistance can be provided, even in a poorlubrication state where the lubricating oil is insufficiently supplied.

Also, according to this embodiment, a swash plate can be provided whichis suitable as a swash plate 3 for a swash plate type compressor used ina severe environment with a new coolant or a CO₂ coolant.

Further, in the conventional swash plate, the relatively expensiveintermediate layer, such as a metal layer, a plated layer or a chemicalconversion coating layer, is provided on the surface of the substrate 11but such an intermediate layer is omitted in this embodiment. Thus,according to this embodiment, one step of the production process of theswash plate 3 can be omitted, which can reduce the production costs ofthe swash plate 3.

Multiple concentric annular grooves may be formed instead of the spiralannular groove 12A provided in the surface of the first resin layer 12.With such a configuration, the same operation and effect as theabove-described embodiment can be obtained.

In the embodiment, the iron-based substrate 11 is used but an aluminum-or copper-based substrate 11 may also be used.

REFERENCE SIGNS LIST

-   3 . . . swash plate-   3A, 3B . . . sliding surface-   4 . . . shoe-   11 . . . substrate-   12 . . . first resin layer-   12A . . . annular groove-   13 . . . second resin layer

The invention claimed is:
 1. A swash plate having a sliding surface thatslides with respect to a shoe, consisting of: a substrate made of amaterial selected from the group consisting of an iron-based material,an aluminum-based material and a copper-based material and having a flatsurface; a first resin layer having a thickness of 3-70 μm coated on theflat surface of the substrate and having a spiral annular groove or aplurality of concentric annular grooves formed in an outer surfacethereof; and a second resin layer having a hardness less than that ofthe first resin layer and a thickness of 1-40 μm coated on the firstresin layer to match the sectional shape of the spiral annular groove ormultiple concentric annular grooves formed in the outer surface of thefirst resin layer and having minute irregularities formed in an entiresurface thereof, the second resin layer consisting of a resin paintcontaining MoS₂ particles and the second resin layer is applied on thefirst resin layer such that the MoS₂ particles are exposed and form theminute irregularities, wherein during the initial stage of sliding withrespect to the shoe, the second resin layer serves as the slidingsurface, after the initial stage of sliding, the second resin layerpartially wears and exposes protrusions of the spiral annular groove orconcentric annular grooves such that the protrusions or concentricannular grooves and the second resin layer adjacent to the protrusionsor concentric annular grooves serve as the sliding surface, alubricating oil is contained in the minute irregularities in the surfaceof the second resin layer, the thickness of the first resin layer isgreater than the thickness of the second resin layer the second resinlayer contains the MoS₂ in an amount of 30-80% by weight andpolytetrafluoroethylene in an amount of 1-30% by weight, the amount ofpolytetrafluoroethylene in the second resin layer is less than theamount of MoS₂ and the first resin layer contains graphite in an amountof 10-50% by weight and MoS₂ or polytetrafluoroethylene in an amount of1-30% by weight, the total amount of MoS₂ or polytetrafluoroethylene inthe first resin layer is less than the amount of graphite.
 2. The swashplate according to claim 1, wherein the first resin layer has athickness of from 5-50 μm and the second resin layer has a thickness offrom 3-10 μm.
 3. The swash plate according to claim 1, wherein thegraphite contained in the first resin layer includes first particleswith a diameter of more than 10 μm and second particles with a diameterof less than 10 μm in a predetermined ratio and thepolytetrafluoroethylene contained in the first resin layer includesthird particles with a diameter of more than 7 μm and fourth particleswith a diameter of less than 7 μm in a predetermined ratio.
 4. The swashplate according to claim 1, wherein a thickness of the protrusions ofthe spiral annular groove in the first resin layer is larger than thethickness of the second resin layer.
 5. The swash plate according toclaim 4, wherein a thickness B of a portion of the second resin layercoating the protrusions of the spiral annular groove in the first resinlayer and a thickness A of a portion of the second resin layer coating arecess of the spiral annular groove have a size relationship of 3/2A≧B.6. The swash plate according to claim 1, wherein the first resin layeris a thermosetting resin binder to which at least one of carbon, MoS₂and PTFE is added.